Pengaruh Feed Rate Terhadap Uji Kekerasan, Uji Tarik dan Mikro Struktur Pada Alumunium 6061 dengan Metode Friction Stir Welding
Main Article Content
Abstract
This research investigates the effect of feed rate on the mechanical and structural properties of friction stir welding (FSW) of aluminium 6061. This method is important because FSW is an environmentally friendly and energy efficient welding technique for applications on aluminium materials and its alloys. The feed rates used are 60 mm/min, 90 mm/min and 120 mm/min. Hardness, tensile and microstructure tests are carried out to understand how feed rate affects material properties. The hardness value of the material also shows a trend that is in line with the tensile strength, with variations in the feed rate parameter having a significant effect on the hardness in the weld metal area, the heat affected zone (HAZ) and the base metal.
Article Details
This work is licensed under a Creative Commons Attribution 4.0 International License.
References
A. Azwinur, S. A. Jalil, and A. Husna, “Pengaruh variasi arus pengelasan terhadap sifat mekanik pada proses pengelasan SMAW,” J. Polimesin, vol. 15, no. 2, p. 36, 2017.
B. L. Sanyoto, N. Husodo, S. Bangun, and S. Mahirul, “Penerapan Teknologi Las Gesek (Friction Welding) Dalam Proses Penyambungan Dua Buah Pipa Logam Baja Karbon Rendah,” J. Energi dan Manufaktur, vol. 5, no. Oktober, pp. 51–60, 2012.
M. B. Waluyo and V. D. Waas, “Pengaruh Laju Pengelasan Terhadap Kekuatan Tarik Pengelasan Friction Stir Welding Material Aluminium,” J. Tek. Mesin, Elektro, Inform. Kelaut. dan Sains, vol. 2, no. 1, pp. 51–55, 2022.
S. Mizhar, Suherman, and R. Fauzi, “Pengaruh Penambahan Magnesium Terhadap Kekerasan , Kekuatan Impak Dan Struktur Mikro Pada Aluminium Paduan ( Al-Si ) Dengan Metode Lost Foam Casting,” RisearchGate, vol. 2, no. November 2016, pp. 77–84, 2018.
I. Saefuloh, A. Pramono, W. Jamaludin, and I. Rosyadi, “Studi Karakterisasi Sifat Mekanik Dan struktur Mikro Material Piston Alumunium-Silikon Alloy,” Flywheel J. Tek. mesin Untirta, vol. IV, no. 2, pp. 56–62, 2018.
D. Prasetyo Koesgi, Sehono, and D. Wicaksono, “Pengaruh Pemanasan Awal Terhadap Sifat Mekanik Sambungan Spot Friction Stir Welding Dalam Pemasangan Rivet Alumunium 2024,” Tek. STTKD J. Tek. Elektron. Engine, vol. 7, no. 1, pp. 140–153, 2021.
A. Heidarzadeh et al., “Friction Stir Welding/processing of metals and alloys: A comprehensive review on microstructural evolution,” Prog. Mater. Sci., vol. 117, no. March 2019, p. 100752, 2021.
P. Pujono, D. Prabowo, I. Kurniawan, J. S. Pribadi, and M. Yusuf, “Laju perambatan retak fatik dan sifat mekanik pada pengelasan Friction Stir Welding (FSW) aluminium AA2024-T3 dengan perlakuan transient thermal tensioning (TTT),” Turbo J. Progr. Stud. Tek. Mesin, vol. 11, no. 2, pp. 293– 300, 2022.
G. K. C. J. Rogo, Suharno, and Yadiono, “Pengaruh Variasi Suhu Tuang Terhadap Kekerasan Dan Struktur Mikro Pada Hasil Remelting Aluminium Tromol Supra X Dengan Cetakan Logam,” J. Nosel, vol. 2, no. 2, 2013.
M. Hariz, D. Sayogi, M. N. Sasongko, T. Mesin, and U. Brawijaya, “Analisis Temperatur Retreating Side dan Advencing Side Sambungan Las Friction Stir Welding AA 6061 Pada Perbedaan Suhu Awal,” vol. 2, no. April, pp. 633–639, 2023.
K. Roziqin, H. Purwanto, and I. Syafa’at, “Pengaruh Model Sistem Saluran Pada Proses Pengecoran Aluminium Daur Ulang Terhadap Struktur Mikro Dan Kekerasan Coran Pulli Diameter 76 mm dengan Cetakan Pasir,” J. Momentum UNWAHAS, vol. 8, no. 1, p. 114152, 2012.
H. Purwanto et al., “Evaluasi Laju Pengelasan terhadap Mikrostruktur Sambungan Aluminium 5052 dengan Menggunakan Metode Friction Stir Welding,” vol. 6, no. 2, pp. 1–7, 2022.
W. P. Aji and A. Supriyanto, “Studi Eksperimen Uji Kekerasan Dan Foto Mikro Material Komposit Alumunium - Silikon Metode Metalurgi Serbuk,” Teknika, vol. 7, no. 2, pp. 93–98, 2021.
N. Kholis, “Analisis Hasil Double Side Friction Stir Welding pada Aluminium AA6061 dengan Penguat Serbuk Cu terhadap Struktur Mikro,” Suara Teknik , vol. 14, no. 1, pp. 1–6, 2023.